Journal of Dental Research Mar 2023There have been significant advances in adhesive dentistry in recent decades, with efforts being made to improve the mechanical and bonding properties of resin-based... (Review)
Review
There have been significant advances in adhesive dentistry in recent decades, with efforts being made to improve the mechanical and bonding properties of resin-based dental adhesive materials. Various attempts have been made to achieve versatility, introducing functional monomers and silanes into the materials' composition to enable the chemical reaction with tooth structure and restorative materials and a multimode use. The novel adhesive materials also tend to be simpler in terms of clinical use, requiring reduced number of steps, making them less technique sensitive. However, these materials must also be reliable and have a long-lasting bond with different substrates. In order to fulfill these arduous tasks, different chemical constituents and different techniques are continuously being developed and introduced into dental adhesive materials. This critical review aims to discuss the concepts behind novel monomers, bioactive molecules, and alternative techniques recently implemented in adhesive dentistry. Incorporating monomers that are more resistant to hydrolytic degradation and functional monomers that enhance the micromechanical retention and improve chemical interactions between adhesive resin materials and various substrates improved the performance of adhesive materials. The current trend is to blend bioactive molecules into adhesive materials to enhance the mechanical properties and prevent endogenous enzymatic degradation of the dental substrate, thus ensuring the longevity of resin-dentin bonds. Moreover, alternative etching materials and techniques have been developed to address the drawbacks of phosphoric acid dentin etching. Altogether, we are witnessing a dynamic era in adhesive dentistry, with advancements aiming to bring us closer to simple and reliable bonding. However, simplification and novelty should not be achieved at the expense of material properties.
Topics: Dental Cements; Dental Bonding; Resin Cements; Acid Etching, Dental; Dental Materials; Materials Testing; Dentin-Bonding Agents; Dentin; Composite Resins
PubMed: 36694473
DOI: 10.1177/00220345221145673 -
International Journal of Molecular... Nov 2022The aim of the study was to analyze the chemical−physical properties and bioactivity (apatite-forming ability) of three recently introduced premixed bioceramic root...
The aim of the study was to analyze the chemical−physical properties and bioactivity (apatite-forming ability) of three recently introduced premixed bioceramic root canal sealers containing varied amounts of different calcium silicates (CaSi): a dicalcium and tricalcium silicate (1−10% and 20−30%)-containing sealer with zirconium dioxide and tricalcium aluminate (CERASEAL); a tricalcium silicate (5−15%)-containing sealer with zirconium dioxide, dimethyl sulfoxide and lithium carbonate (AH PLUS BIOCERAMIC) and a dicalcium and tricalcium silicate (10% and 25%)-containing sealer with calcium aluminate, tricalcium aluminate and tantalite (NEOSEALER FLO). An epoxy resin-based sealer (AH PLUS) was used as control. The initial and final setting times, radiopacity, flowability, film thickness, open pore volume, water absorption, solubility, calcium release and alkalizing activity were tested. The nucleation of calcium phosphates and/or apatite after 28 days aging in Hanks balanced salt solution (HBSS) was evaluated by ESEM-EDX, vibrational IR and micro-Raman spectroscopy. The analyses showed for NeoSealer Flo and AH Plus the longest final setting times (1344 ± 60 and 1300 ± 60 min, respectively), while shorter times for AH Plus Bioceramic and Ceraseal (660 ± 60 and 720 ± 60 min, respectively). Radiopacity, flowability and film thickness complied with ISO 6876/12 for all tested materials. A significantly higher open pore volume was observed for NeoSealer Flo, AH Plus Bioceramic and Ceraseal when compared to AH Plus (p < 0.05), significantly higher values were observed for NeoSealer Flo and AH Plus Bioceramic (p < 0.05). Ceraseal and AH Plus revealed the lowest solubility. All CaSi-containing sealers released calcium and alkalized the soaking water. After 28 days immersion in HBSS, ESEM-EDX analyses revealed the formation of a mineral layer that covered the surface of all bioceramic sealers, with a lower detection of radiopacifiers (Zirconium for Ceraseal and AH Plus Bioceramic, Tantalum for NeoSealer Flo) and an increase in calcium, phosphorous and carbon. The calcium phosphate (CaP) layer was more evident on NeoSealer Flo and AH Plus Bioceramic. IR and micro-Raman revealed the formation of calcium carbonate on the surface of all set materials. A thin layer of a CaP phase was detected only on AH Plus Bioceramic and NeoSealer Flo. Ceraseal did not show CaP deposit despite its highest calcium release among all the tested CaSi-containing sealers. In conclusion, CaSi-containing sealers met the required chemical and physical standards and released biologically relevant ions. Slight/limited apatite nucleation was observed in relation to the high carbonation processes.
Topics: Root Canal Filling Materials; Calcium; Dental Pulp Cavity; Silicates; Water; Apatites
PubMed: 36430393
DOI: 10.3390/ijms232213914 -
Biomaterials Sep 2021Our goal was to generate functionalized 3D-printed scaffolds for bone regeneration using silk-hydroxyapatite bone cements and osteoinductive, proangiogenic and...
Our goal was to generate functionalized 3D-printed scaffolds for bone regeneration using silk-hydroxyapatite bone cements and osteoinductive, proangiogenic and neurotrophic growth factors or morphogens for accelerated bone formation. 3D printing was utilized to generate macroporous scaffolds with controlled geometries and architectures that promote osseointegration. We build on the knowledge that the osteoinductive factor Bone Morphogenetic Protein-2 (BMP2) can also positively impact vascularization, Vascular Endothelial Growth Factor (VEGF) can impact osteoblastic differentiation, and that Neural Growth Factor (NGF)-mediated signaling can influence bone regeneration. We assessed functions on the 3D printed construct via the osteogenic differentiation of human mesenchymal stem cells; migration and proliferation of human umbilical vein endothelial cells; and proliferation of human induced neural stem cells. The scaffolds provided mechanical properties suitable for bone and the materials were cytocompatible, osteoconductive and maintained the activity of the morphogens and cytokines. Synergistic outcomes between BMP-2, VEGF and NGF in terms of osteoblastic differentiation in vitro were identified, based on the upregulation of genes associated with osteoblastic differentiation (Runt-related transcription factor-2, Osteopontin, Bone Sialoprotein). Additional studies will be required to assess these scaffold designs in vivo. These results are expected to have a strong impact in bone regeneration in dental, oral and maxillofacial surgery.
Topics: Bone Regeneration; Durapatite; Human Umbilical Vein Endothelial Cells; Humans; Osteogenesis; Printing, Three-Dimensional; Silk; Tissue Engineering; Tissue Scaffolds; Vascular Endothelial Growth Factor A
PubMed: 34256231
DOI: 10.1016/j.biomaterials.2021.120995 -
Anatolian Journal of Cardiology Mar 2022
Topics: Bone Cements; Heart Injuries; Humans
PubMed: 35346920
DOI: 10.5152/AnatolJCardiol.2021.1404 -
Biomedicines Jan 2021Bone cement is used as a mortar for securing bone implants, as bone void fillers or as spacers in orthopaedic surgery. Antibiotic-loaded bone cements (ALBCs) have been... (Review)
Review
Bone cement is used as a mortar for securing bone implants, as bone void fillers or as spacers in orthopaedic surgery. Antibiotic-loaded bone cements (ALBCs) have been used to prevent and treat prosthetic joint infections by providing a high antibiotic concentration around the implanted prosthesis. High antibiotic concentrations are, on the other hand, often associated with tissue toxicity. Controlling antibiotic release from ALBCS is key to achieving effective infection control and promoting prosthesis integration with the surrounding bone tissue. However, current ALBCs still need significant improvement in regulating antibiotic release. In this review, we first provide a brief introduction to prosthetic joint infections, and the background concepts of therapeutic efficacy and toxicity in antibiotics. We then review the current state of ALBCs and their release characteristics before focusing on the research and development in controlling the antibiotic release and osteo-conductivity/inductivity. We then conclude by a discussion on the need for better in vitro experiment designs such that the release results can be extrapolated to predict better the local antibiotic concentrations in vivo.
PubMed: 33401484
DOI: 10.3390/biomedicines9010026 -
Cureus Nov 2023Calcium silicate-based types of cement have gained recognition in various dental applications due to their exceptional sealing capabilities, bioactivity, and minimal...
INTRODUCTION
Calcium silicate-based types of cement have gained recognition in various dental applications due to their exceptional sealing capabilities, bioactivity, and minimal adaptability. However, these materials have certain shortcomings that can lead to mechanical failures and premature degradation. The inclusion of metal ions into their structure is expected to promote their biological activity. This article focuses on the preparation and characterization of calcium silicate cement to enhance its fundamental material properties, by introducing zinc and silver while retaining its biomaterial characteristics.
AIM
This study aims to evaluate the biomedical potential of zinc and silver-impregnated bioactive calcium silicate cement.
MATERIALS AND METHODS
The calcium silicate powder was synthesized via the sol-gel method. Tetraethyl orthosilicate, calcium nitrate, silver nitrate, and zinc nitrate were sequentially added to create the bioactive calcium silicate material. The synthesized particles underwent physicochemical characterization using techniques such as scanning electron microscopy, X-ray diffraction, Raman spectroscopy, and biological characterization through in vitro hemocompatibility assays.
RESULTS
The study's results revealed the presence of multiple crystalline phases (AgSiO, ZnSiO, CaCO) as indicated by X-ray diffraction. Raman spectra displayed vibrations associated with Si-O-Si and Zn-O bonding in the zinc and silver-infused bioactive calcium silicate. Scanning electron microscopy confirmed a mixture of spherical and sheet-like morphologies, while energy dispersive spectra confirmed the presence of elements Ca, Si, Zn, Ag, O, and C. In vitro hemocompatibility testing affirmed the material's biocompatible nature.
CONCLUSION
In conclusion, the zinc and silver-infused calcium silicate cement was successfully synthesized through an in-house procedure and demonstrated biocompatibility. The inclusion of zinc and silver, known for their osteogenic and antimicrobial properties, is anticipated to enhance the cement's biological properties and broaden its utility in dentistry. Further in vitro and in vivo investigations are imperative to validate its clinical applications and elucidate the molecular mechanisms underlying its efficacy.
PubMed: 38054157
DOI: 10.7759/cureus.48243 -
Materials (Basel, Switzerland) Feb 2022To develop an endodontic cement using bovine bone-derived hydroxyapatite (BHA), Portland cement (PC), and a radiopacifier. BHA was manufactured from waste bovine bone...
To develop an endodontic cement using bovine bone-derived hydroxyapatite (BHA), Portland cement (PC), and a radiopacifier. BHA was manufactured from waste bovine bone and milled to form a powder. The cements were developed by the addition of BHA (10%/20%/30%/40% wt), 35% wt, zirconium oxide (radiopacifier) to Portland cement (PC). A 10% nanohydroxyapatite (NHA) cement containing PC and a radiopacifier, and a cement containing PC (PC65) and a radiopacifier were also manufactured as controls. The cements were characterised to evaluate their compressive strength, setting time, radiopacity, solubility, and pH. The biocompatibility was assessed using Saos-2 cells where ProRoot MTA acted as the control. Compressive strength, solubility and pH were evaluated over a 4-week curing period. The compressive strength (CS) of all cements increased with the extended curing times, with a significant CS increase in all groups from day 1 to day 28. The BHA 10% exhibited significantly higher CS compared with the other cements at all time points investigated. The BHA 10% and 20% groups exhibited significantly longer setting times than BHA 30%, 40% and PC65. The addition of ZrO in concentrations above 20% wt and TaO at 30% wt resulted in a radiopacity equal to, or exceeding that of, ProRoot MTA. The experimental cements exhibited relatively low cytotoxicity, solubility and an alkaline pH. The addition of 10% and 20% BHA to an experimental PC-based cement containing 35% ZrO improved the material's mechanical strength while enabling similar radiopacity and biocompatibility to ProRoot MTA. Although BHA is a cost-effective, biomimetic additive that can improve the properties of calcium silicate endodontic cements, further studies are now warranted to determine its clinical potential.
PubMed: 35161119
DOI: 10.3390/ma15031176 -
BioMed Research International 2022The purpose of this study to explore strategies for reducing cement leakage during cement-augmented pedicle screw fixation, we compared the cement distribution patterns...
The purpose of this study to explore strategies for reducing cement leakage during cement-augmented pedicle screw fixation, we compared the cement distribution patterns and biomechanical strengths of different types of cement-augmented fenestrated screws and traditional cement-augmented techniques. We compared five screw groups in this study: (1) Cannulated screws (Cann); (2) distal one-hole screws (D1); (3) distal two-hole screws (D2); (4) middle two-hole screws (M2); and (5) traditional screws with a traditional cement injection technique (Trad). The screws were inserted into cancellous bone blocks using a controlled, adequate cement injection pressure (1.6-2.0 kg), and an appropriate cement viscosity. Center to screw tip distance, three-dimensional distribution, and pull-out strength for cement were compared between groups. The average distance between the cement center and the screw tip was highest in the M2 group, suggesting a higher risk of cement leakage into the spinal canal. The Trad group had the highest migration distance in the -axis, also reflecting a higher risk of leakage into the spinal canal. The D1 group had the highest pull-out strength (253 ± 48.82 N and 797 ± 58.31 N) in bone blocks representing different degrees of osteoporosis, and the D2 group had the second highest pull-out strength in the severe osteoporosis model. Overall, D1 screws appeared to be the best option for optimizing biomechanical function and minimizing the risk of cement leakage into the spinal canal in patients with osteoporotic bone undergoing spinal surgery.
Topics: Humans; Pedicle Screws; Bone Cements; Osteoporosis; Bone and Bones; Glass Ionomer Cements; Biomechanical Phenomena; Lumbar Vertebrae
PubMed: 36303583
DOI: 10.1155/2022/8293524 -
Genesis (New York, N.Y. : 2000) Sep 2022The periodontium is comprised of multiple units of mineralized and nonmineralized tissues including the cementum on the root surface, the alveolar bone, periodontal... (Review)
Review
The periodontium is comprised of multiple units of mineralized and nonmineralized tissues including the cementum on the root surface, the alveolar bone, periodontal ligament (PDL), and the gingiva. PDL contains a variety of cell populations including mesenchymal stem/progenitor cells (MSCs) termed PDLSCs, which contribute to periodontal regeneration. Recent studies utilizing mouse genetic models shed light on the identities of these mesenchymal progenitors in their native environment, particularly regarding how they contribute to homeostasis and repair of the periodontium. The current concept is that mesenchymal progenitors in the PDL are localized to the perivascular niche. Single-cell RNA sequencing (scRNA-seq) analyses reveal heterogeneity and cell-type specific markers of cells in the periodontium, as well as their developmental relationship with precursor cells in the dental follicle. The characteristics of PDLSCs and their diversity in vivo are now beginning to be unraveled thanks to insights from mouse genetic models and scRNA-seq analyses, which aid to uncover the fundamental properties of stem cells in the human PDL. The new knowledge will be highly important for developing more effective stem cell-based regenerative therapies to repair periodontal tissues in the future.
Topics: Animals; Cells, Cultured; Humans; Mesenchymal Stem Cells; Mice; Periodontal Ligament; Periodontium; Stem Cells
PubMed: 35916433
DOI: 10.1002/dvg.23495 -
Australian Dental Journal Sep 2015Carious affected dentine (CAD) represents a very common substrate in adhesive dentistry. Despite its ability to interact with adhesive systems, the intrinsic character... (Review)
Review
BACKGROUND
Carious affected dentine (CAD) represents a very common substrate in adhesive dentistry. Despite its ability to interact with adhesive systems, the intrinsic character of CAD leads to lower bonding compared with sound dentine, regardless of the adhesive systems used. This low bonding may be more susceptible to leakage and hydrolysis of the interface by matrix metalloproteinases (MMPs). This systematic review aimed to determine current knowledge of CAD bonding, together with bond strength and MMP inhibitors' ability to prevent hybrid layer instability.
METHODS
MEDLINE/Pubmed, Scopus and The Cochrane Library databases were electronically searched for articles published from 1 January 1960 to 31 August 2014. Two reviewers independently screened and included papers according to predefined selection criteria.
RESULTS
The electronic searches identified 320 studies. After title, abstract and full-text examinations, 139 articles met the inclusion criteria. Data highlighted that a poor resin saturation of the already demineralized collagen matrix in CAD is strictly related to nanoleakage in interdiffusion and is the basis of the progressive decrease in strength with hydrolysis by MMPs. The use of mild self-etching systems seems to be the more accredited method to establish bonding in CAD. Inhibitors of MMPs may ensure better performance of CAD bonding, allowing undisturbed remineralization of the affected matrix.
CONCLUSIONS
CAD bonding needs further understanding and improvement, particularly to enhance the strength and durability of the hybrid layer.
Topics: Dental Bonding; Dental Caries; Dental Cements; Dental Leakage; Dentin; Humans; Matrix Metalloproteinase Inhibitors; Stress, Mechanical
PubMed: 25790344
DOI: 10.1111/adj.12309